TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
53
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
44
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4.5
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
20
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
3300
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
95
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
3200
|
MPa
|
ASTM D 790
|
|
Tensile Stress, yield, 5 mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
43
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
4.5
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
12.5
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
3300
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
90
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
3300
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
280
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
110
|
J/m
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
40
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*3 +23°C
|
25
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*3 -30°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
25
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
15
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
145
|
°C
|
ASTM D 1525
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
135
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
4.07E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
6.94E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
4.07E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
6.94E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 75°C +/- 2°C
|
PASS
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
144
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
146
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
134
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.25
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.2 - 0.6
|
%
|
SABIC Method
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
11
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.25
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.12
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.46
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
10
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
1.78E+17
|
Ohm-cm
|
ASTM D 257
|
|
Surface Resistivity
|
2.86E+17
|
Ohm
|
ASTM D 257
|
|
Dielectric Strength, in oil, 1.6 mm
|
31.5
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 1 MHz
|
3.04
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.0086
|
-
|
ASTM D 150
|
|
Dielectric Constant, 1.9 GHz
|
2.95
|
-
|
SABIC Method
|
|
Dissipation Factor, 1.9 GHz
|
0.0057
|
-
|
SABIC Method
|
點(diǎn)擊圖片查看大圖
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。