點(diǎn)擊圖片查看大圖PA66高沖擊 RBG16I 美國LNP 玻璃微珠增強(qiáng)PA
LNP LUBRICOMP RBG16I is a compound based on Nylon 66 resin containing Glass Bead, Graphite. Added features of this material include: High Impact.
LNP LUBRICOMP RBG16I是一種基于尼龍66樹脂的化合物，含有玻璃珠、石墨。這種材料的附加特性包括：高沖擊性。
RBG16I物性表：
| REVISION: 10/12/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yield, 5 mm/min | 64 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3500 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| CTE, 23°C to 60°C, flow | 7.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 7.9E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 223 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.4 | % | SABIC method | |
| Density | 1.37 | g/cm3 | ISO 1183 | |
RA004
LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing 20% Aramid. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RAL22
LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RAL229
LNP LUBRICOMP RAL229 is a compound based on Nylon 66 containing 10% Aramid, 10% PTFE. Added features of this grade include: Flame Retardant, Wear Resistant.EUROPEASIAAMERICAS
RAL22I
LNP LUBRICOMP RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact.ASIAAMERICAS
RAL22S
LNP LUBRICOMP RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RAL23
LNP LUBRICOMP* RAL23 is a compound based on Nylon 66 resin containing 15% Aramid Fiber, 10% PTFE. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RAL23S
LNP LUBRICOMP* RAL23S is a compound based on Nylon 66 resin containing 10% PTFE, 15% Aramid. Added features of this material include: Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RAL32
LNP* LUBRICOMP* RAL32 is a compound based on Nylon 66 resin containing 10% Aramid, 15% PTFE. Added feature of this grade is: Wear Resistant.EUROPEASIAAMERICAS
RAP22
LNP LUBRICOMP RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant.EUROPEASIAAMERICAS
RBG16I
LNP LUBRICOMP RBG16I is a compound based on Nylon 66 resin containing Glass Bead, Graphite. Added features of this material include: High Impact.EUROPEASIAAMERICAS
LNP LUBRICOMP RBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant.EUROPEASIAAMERICAS
RCL26
LNP LUBRICOMP RCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.EUROPEASIAAMERICAS
RCL34
LNP LUBRICOMP RCL34 is a compound based on Nylon 66 containing 20% Carbon Fiber, 15% PTFE. Added features of this grade includes: Wear Resistant, Electrically Conductive.EUROPEAMERICAS
RCL36
LNP LUBRICOMP RCL36 is a compound based on Nylon 66 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wesr Resistant, Electrically Conductive.EUROPEAMERICAS
RCL36S
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Heat Stabilized.EUROPEASIAAMERICAS
RCP36
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant.EUROPEASIAAMERICAS
REL22
LNP LUBRICOMP REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.EUROPEASIAAMERICAS
RFG16
LNP LUBRICOMP RFG16 is a compound based on PA 66 resin containing Glass Fiber, Graphite. Added features include: Internally Lubricated.EUROPEASIAAMERICAS
RFI12
LNP LUBRICOMP RFI12 is a compound based on Nylon 66 resin containing 10% Glass Fiber, 2% Silicone. Added feature of this material is: Wear Resistant.EUROPEASIAAMERICAS
RFL16
LNP LUBRICOMP RFL16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant.ASIAAMERICAS
RFL22E
LNP LUBRICOMP RFL22E Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated, Easy MouldingEUROPEASIAAMERICAS
RFL26
LNP LUBRICOMP* RFL26 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RFL26S
LNP LUBRICOMP RFL26S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.EUROPEASIAAMERICAS
RFL32
LNP LUBRICOMP RFL32 is a compound based on Nylon 66 containing 10% Glass Fiber, 15% PTFE. Added feature of this material includes: Wear Resistant.EUROPEASIAAMERICAS
RFL33
LNP LUBRICOMP RFL33 is a compound based on Nylon 66 resin containing 15% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.EUROPEASIAAMERICAS
RFL34
LNP LUBRICOMP RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.EUROPEASIAAMERICAS
RFL36
LNP LUBRICOMP RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Wear ResistantEUROPEASIAAMERICAS
RFL369
LNP LUBRICOMP RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricatedEUROPEASIAAMERICAS
RFL36L
LNP LUBRICOMP RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.EUROPEASIAAMERICAS
RFL36S
LNP LUBRICOMP RFL36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.EUROPEAMERICAS
RFL36SXS
LNP LUBRICOMP RFL36SXS is a compound based on PA 66 resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized.EUROPEASIAAMERICAS
RFL36U
LNP LUBRICOMP RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized.EUROPEASIAAMERICAS
RFL36XXY
LNP LUBRICOMP RFL36XXY is a compound based on Nylon 66 containing 30% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.EUROPEASIAAMERICAS
RFL36XXZ
LNP LUBRICOMP RFL36XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.ASIAAMERICAS
RFL46
LNP LUBRICOMP RFL46 is a compound based on PA66 resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.EUROPEASIAAMERICAS
RFL46ES
LNP LUBRICOMP RFL46ES is a compound based on Nylon 6/6 containing 30% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Easy Molding.EUROPEASIAAMERICAS
RFN14
LNP LUBRICOMP RFN14 is a compound based on Nylon 66 containing 20% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant.EUROPEASIAAMERICAS
RFN16
LNP* LUBRICOMP* RFN16 is a compound based on Nylon 66 resin containing 30% Glass Fiber and MOS2. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RFN169
LNP LUBRICOMP RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant.EUROPEASIAAMERICAS
RFN16S
LNP LUBRICOMP* RFN16S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RFN16SXZ
LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RFN17SXS
LNP LUBRICOMP RFN17SXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat StabilizedEUROPEASIAAMERICAS
RFN18S
LNP LUBRICOMP* RFN18S is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RFN18SXS
LNP LUBRICOMP RFN18SXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.EUROPEASIAAMERICAS
RFN1ASXS
LNP* Lubricomp* RFN1ASXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.EUROPEASIAAMERICAS
RFP36
LNP LUBRICOMP RFP36 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE, Silicone. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RFP36L
LNP* LUBRICOMP* RFP36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this grade include: Low Extractable, Wear Resistant.EUROPEASIAAMERICAS
RFP38
LNP LUBRICOMP RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.EUROPEASIAAMERICAS
RFP48SXS
LNP LUBRICOMP RFP48SXS is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Heat Stabilized.EUROPEASIAAMERICAS
RI001
LNP LUBRICOMP RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant.EUROPEAMERICAS
RKN14
LNP LUBRICOMP RKN14 is a compound based on Nylon 66 resin containing Mineral, MOS2.EUROPEASIAAMERICAS
RL002
LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant.EUROPEAMERICAS
RL003
LNP LUBRICOMP RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant.EUROPEAMERICAS
RL0039XP
LNP LUBRICOMP RL0039XP is a compound based on PA66 resin containing PTFE, Flame Retardant. Added features include ; Flame Retardant, internally Lubricated.EUROPEASIAAMERICAS
RL004
LNP LUBRICOMP RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant.EUROPEAMERICAS
RL0049S
LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RL004S
LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.EUROPEAMERICAS
RL008
LNP LUBRICOMP RL008 is a compound based on PA 66 containing PTFE. Added features include: Internally Lubricated.EUROPEASIAAMERICAS
RL4040HSUV
LNP* LUBRICOMP* RL4040HSUV is a compound based on Nylon 66 containing 20% PTFE. Added features of this grade include: Heat Stabilized, UV Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RN001
LNP* Lubricomp* RN001 is a compound based on Nylon 66 resin containing MOS2.EUROPEASIAAMERICAS
RN001S
LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized.EUROPEASIAAMERICAS
RP002
LNP LUBRICOMP RP002 is a compound based on PA 66 resin containing PTFE, Silicone: Added features include; Internallly Lubricated.EUROPEASIAAMERICAS
RP003
LNP LUBRICOMP RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.ASIAAMERICAS
RP004
LNP LUBRICOMP* RP004 is a compound based on Nylon 66 resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant.EUROPEASIAAMERICAS
RP004S
LNP LUBRICOMP RP004S is a compound based on Nylon 66 containing PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant.EUROPEASIAAMERICAS
RP004SZ
LNP* LUBRICOMP RP004SZ is a compound based on Nylon 66 containing 20% PTFE/Silicone. Added features of this grade include: Heat Stabilized, Extrusion Grade, Wear Resistant.EUROPEASIAAMERICAS
RX03643H
LNP LUBRICOMP RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.EUROPEASIAAMERICAS
RX05495
LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing 30% Glass Bead, Graphite, Glass Fiber, 5% Graphite Powder. Added features of this material include: Easy Molding. Heat Stabilized, Mold Release, Wear Resistant.EUROPEASIAAMERICAS
RX85514
LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.EUROPEASIAAMERICAS
RZL16
LNP* LUBRICOMP* RZL16 is a compound based on Nylon 66 resin containing 30% Milled Glass, 5% PTFE. Added feature of this grade is: Wear Resistant.EUROPEASIAAMERICAS
RZL36
LNP LUBRICOMP RZL36 is a compound based on PA 66 resin containing Milled Glass, PTFE. Added features include: Internally Lubricated.
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對此不承擔(dān)任何保證責(zé)任。我們原則上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請?jiān)敿?xì)核實(shí)對方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報(bào)。
簡繁切換